| 品名：铍青铜 | 牌号：MoldMAX XL | 产地：美国 |
| 铜含量：标准% | 杂质含量：微量% | 粒度：微量目 |
| 软化温度：标准℃ | 导电率：微量%IACS | 硬度：180-200HRB |
| 品牌：进口 |
MoldMAX XL? Alloy
Materion Brush Performance Alloys’ MoldMAX XL Alloy is a high strength copper mold alloy with good thermal conductivity.The alloy contains no beryllium and is available in sections as large as 12” thick. The alloy’s hardness is comparable with AISI P-20tool steel, but its thermal conductivity is two to three times higher. MoldMAX XL Alloy is used as injection mold cores andcavities. The alloy provides excellent toughness, wear resistance and surface finish. MoldMAX XL Alloy typically machines fasterthan tool steels, and with appropriate machine tools, metal removal rates several times higher can be obtained
CHEMICAL COMPOSITION (weight percent)
| Alloy | Nickel | Tin | Copper |
| MoldMAX XL Alloy | 8.5-9.5 | 5.5-6.5 | Balance |
PHYSICAL PROPERTIES
| Elastic Modulus | Melting Point (Solidus | Density | Thermal Expansion | Thermal Conductivity (100 °C) | Heat Capacity (100 °C) |
| 17,000 ksi 120 GPa | ~1695 °F ~925 °C | 0.322 lb/in3 8.90 g/cm3 | 9.0x10-6 in/in °F 16.2 x 10-6 °C -1 | 40 BTU/hr·ft·°F 70 W/m·°C | 0.093 BTU/lb·°F 0.39 J/g·°C |
TYPICAL MECHANICAL PROPERTIES*
| 0.2% Offset Yield Strength (nominal) | Ultimate Tensile Strength | Fatigue Strength 107 Cycles (R=-1) | Elongation | Impact Strength | Hardness |
| 105 ksi 720 MPa | 115 ksi 790 MPa | 35 ksi 240 MPa | 6% | 15 ft·lb 20 J | 30 HRC |
*Properties may vary by shape and thickness.